PVC Type II
PVC Type II Overview
What is the Material: PVC Type II is an amorphous material.
Key Material Features: This material is resistant to weathering, corrosion, and fire.
Other Considerations: This material is beneficial in applications requiring impact resistance. It is material is more impact resistant than PVC Type I, but chemical resistance is improved in PVC Type I.
Physical
| Property | Value | Typical ASTM Test |
|---|---|---|
| Chemical Designation | (PVC) Polyvinyl Chloride Type II | |
| Trade Names (®, ™) | Vintec II | |
| Color | Grey | |
| Density (g/cm^3) | 1.35 | D 792 |
Mechanical
| Property | Value | Typical ASTM Test |
|---|---|---|
| Modulus of Elasticity (Tensile Test) (psi) | 396000 | D 638 |
| Tensile Strength at Yield (psi) | 7400 | D 638 |
| Modulus of Elasticity (Flexural Test) (psi) | 400000 | D 790 |
| Impact Strength (Izod) (ft-lbs/in) | 14 | D 256 |
| Hardness (R) | 106 | D 785 |
| Hardness (D) | 85 | D 785 |
Thermal
| Property | Value | Typical ASTM Test |
|---|---|---|
| Vicat Softening Point (°F) | 181 | |
| Deflection Temperature (°F) (66 psi) | 179 | D 648 |
| Deflection Temperature (°F) (264 psi) | 176 | D 648 |
| Thermal Expansion (CLTE) (in/in/°F) | 3.50E-5 | D 696 |
Electrical
| Property | Value | Typical ASTM Test |
|---|---|---|
| Volume Resistivity (Ω*cm) | 6.00E15 | D 257 |
| Dielectric Strength (V/mil) | 645 | D 149 |
| Dissipation Factor (60 Hz) | 0.0083 | D 150 |
| Dielectric Constant (60 Hz and 50% RH) | 3.03 | D 150 |
Other
| Property | Value | Typical ASTM Test |
|---|---|---|
| Moisture Absorption (%) (24 Hours) | 0.16 | D 570 |
| Flammability | V-0 |
The data stated are typical values intended for reference and comparison purposes only. The data should not be used as a basis for design specifications or quality control. The information is provided as a guide to the best of our knowledge and given without obligation or liability. Testing under individual application circumstances is recommended.