PBT Lubricated
PBT Lubricated Overview
What is the Material: PBT Lubricated is a semi-crystalline material filled with a proprietary lubricant and PTFE (Teflon).
Key Material Features: This material is beneficial in applications requiring a lower coefficient of friction and higher wear resistance, while maintaining properties of other PBT materials including including impact resistance, chemicals resistance, and low moisture absorption.
Other Considerations: It has diverse resistance to many common cleaning chemicals. This material has higher impact resistance than PET.
Physical
| Property | Value | Typical ASTM Test |
|---|---|---|
| Chemical Designation | (PBT) Polybutylene Terephthalate | |
| Trade Names (®, ™) | Hydex 4101L | |
| Filler | Proprietary Lubricant, PTFE | |
| Color | Natural White | |
| Density (g/cm^3) | 1.36 | D 792 |
Mechanical
| Property | Value | Typical ASTM Test |
|---|---|---|
| Modulus of Elasticity (Tensile Test) (psi) | 350000 | D 638 |
| Tensile Strength at Yield (psi) | 6600 | D 638 |
| Elongation at Yield (%) | 30 | D 638 |
| Flexural Strength (psi) | 11500 | D 790 |
| Modulus of Elasticity (Flexural Test) (psi) | 350000 | D 790 |
| Compression Strength: 10% Strain (psi) | 10500 | D 695 |
| Compression Modulus (psi) | 275000 | D 695 |
| Impact Strength (Izod) (ft-lbs/in) | 0.9 | D 256 |
| Hardness (R) | 115 | D 785 |
| Hardness (M) | 75 | D 785 |
| Coefficient of Friction (Kinetic, 40 psi, 50 fpm) | 0.11 | D 3702 |
| Coefficient of Friction (Static) | 0.08 | D 3702 |
Thermal
| Property | Value | Typical ASTM Test |
|---|---|---|
| Deflection Temperature (°F) (264 psi) | 195 | D 648 |
| Service Temperature Continuous (°F) | 221 |
Other
| Property | Value | Typical ASTM Test |
|---|---|---|
| Moisture Absorption (%) (24 Hours) | 0.07 | D 570 |
The data stated are typical values intended for reference and comparison purposes only. The data should not be used as a basis for design specifications or quality control. The information is provided as a guide to the best of our knowledge and given without obligation or liability. Testing under individual application circumstances is recommended.